Technical Details
| Fabric Specifications | |
| Face | 100% Vinyl |
| Backing | 100% Polyester |
| Weight | 30.0 oz. per linear yd |
| Thickness | 1.10 mm |
| Width | 54" |
| Ends/Picks | Ends: 0 per inch Picks: 0 per inch |
| Directional | Yes |
| Railroaded | No |
| Additional Attributes | |
| Resilience™ | Yes |
| Bleach Cleanable | Yes Ratio: 90% Water / 10% Bleach Solution |
| Antibacterial | Yes |
| Antimicrobial | Yes |
| BPA Free | Yes |
| Formaldehyde Free | Yes |
| Free of Conflict Minerals | Yes |
| Lead Free | Yes |
| Mildew Resistant | Yes |
| 16P Phthalate Free | Yes |
| Sulfide Stain Resistant | Yes |
| TRIS Free | Yes |
| Performance Characteristics | |
| Abrasion Resistance ASTM D4157 | 250,000 double rubs* |
| Tensile Strength CFFA-17 | Warp: 121.0 lbs. Fill: 125.0 lbs. |
| Tear Strength CFFA-16b | Warp: 9.8 lbs. Fill: 11.7 lbs. |
| Seam Slippage | Warp: 44.8 lbs. Fill: 53.7 lbs. |
| Colorfastness to Crocking AATCC 8 | Dry: 5.0 Wet: 5.0 |
| UV Resistance AATCC 16 | 500 hours |
| Adhesion CFFA-3 | Warp: 4.31 lbs. Fill: 4.61 lbs. |
| Cold Crack CFFA-6 | -20° F |
| Flex CFFA-10 | 25,000 cycles |
| Flammability** | |
| CAL TB 117-2013 | Passes |
| NFPA 260 | Class 1 |
| UFAC | Class 1 |
| ASTM E-84 | Class A or 1 |
| BIFMA CS-191-53, Sec. 3 | Passes |
| IMO 2010 FTP Part 8, 3.1 & 3.2 | Passes |
| FMVSS 302 | Passes |
| Recommended Cleaning | |
| Please refer to Detailed Cleaning Instructions. |
| Although we try hard to make sure colors on our site are accurate, actual colors may vary. Please order samples prior to making a purchase. | |
| Final determination of the suitability of this product for an application rests with the user. | |
| Proposition 65 Warning: Yes | |
| * Multiple factors affect fabric durability and appearance retention, including end-user application and proper maintenance. Wyzenbeek results above 100,000 double rubs have not been shown to be an indicator of increased lifespan. | |
| ** This term and any corresponding data refer to the typical performance in the specific tests indicated and should not be construed to imply the behavior of this or any other material under actual fire conditions. |