Glaze

SGL-108 Regatta

High Performance Vinyl

FR Free – Compliant with CAL AB 2998
PFAS Free

Flammability Wet Dry Crock Colorfast Phys Prop Abrasion

*

*ACT® Registered Certification Marks

Technical Details

Fabric Specifications
Face 100% Vinyl
Backing 75% Polyester,
25% Cotton
Finish/Treatment Standard Acrylic Topcoat
Weight 36.0 oz. per linear yd
Thickness 1.10 mm
Width 54"
Roll Size 30 yards
Directional Yes
Railroaded No
Additional Attributes
PFAS Free Yes
Prop 65 Compliant Yes
16P Phthalate Free Yes
Free of Added FR Chemicals / CAL AB2998 Compliant Yes
Free of Added Anti-Bacterial Chemicals Yes
Free of Added Anti-Microbial Chemicals Yes
BPA Free Yes
Free of Conflict Minerals Yes
Formaldehyde Free Yes
Free of Heavy Metals Yes
Lead Free Yes
Sulfide Stain Resistant Yes
TRIS Free Yes
Performance Characteristics
Abrasion Resistance ASTM D4157 100,000 double rubs*
Tensile Strength CFFA-17 Warp: 67.0 lbs.
Fill: 78.0 lbs.
Tear Strength CFFA-16 Warp: 7.1 lbs.
Fill: 6.3 lbs.
Seam Slippage CFFA-14 Warp: 67.0 lbs.
Fill: 64.0 lbs.
Colorfastness to Crocking AATCC 8 Dry: 5.0
Wet: 5.0
UV Resistance CFFA-2 300 hours
Adhesion CFFA-3 Warp: 11.0 lbs.
Fill: 9.7 lbs.
Cold Crack CFFA-6 -20° F
Flex CFFA-10 25,000 cycles
Flammability**
CAL TB 117-2013 Passes
NFPA 260 Class 1
UFAC Class 1
ASTM E-84 Class A or 1
BIFMA CS-191-53, Sec. 3 Passes
BIFMA Upholstery, Sec. 4 Passes
Boston Fire Code Passes
IMO 2010 FTP Part 8, 3.1 & 3.2 Passes
FMVSS 302 Passes
Recommended Cleaning
Please refer to Detailed Cleaning Instructions.
Although we try hard to make sure colors on our site are accurate, actual colors may vary. Please order samples prior to making a purchase.
Final determination of the suitability of this product for an application rests with the user.
* Abrasion test results exceeding ACT Performance Guidelines are not an indicator of product lifespan. Multiple factors affect fabric durability and appearance retention.
** This term and any corresponding data refer to the typical performance in the specific tests indicated and should not be construed to imply the behavior of this or any other material under actual fire conditions.