Technical Details

Fabric Specifications
Face 100% Vinyl
Backing 100% Polyester Terry Loop Knit
Finish/Treatment PreFixx® Protective Finish
Bleach Cleanable Yes
Ratio: 90% Water / 10% Bleach Solution
Weight 28.0 oz. per linear yd
Thickness 1.02 mm
Width 54"
Roll Size 40 yards
Directional Yes
Railroaded No
Additional Attributes
Ink Cleanable Yes
PFAS Free Yes
Antibacterial Yes
Antimicrobial Yes
Free of Conflict Minerals Yes
Formaldehyde Free Yes
Free of Heavy Metals Yes
Lead Free Yes
Mildew Resistant Yes
Sulfide Stain Resistant Yes
TRIS Free Yes
Performance Characteristics
Abrasion Resistance CFFA-1a 400,000 double rubs*
Tensile Strength CFFA-17 Warp: 85.0 lbs.
Fill: 75.0 lbs.
Tear Strength CFFA-16c Warp: 20.0 lbs.
Fill: 27.0 lbs.
Seam Slippage CFFA-14 Warp: 35.0 lbs.
Fill: 30.0 lbs.
Colorfastness to Crocking CFFA-7 Dry: 5.0
Wet: 5.0
UV Resistance CFFA-2 650 hours
Adhesion CFFA-3 Warp: 4.0 lbs.
Fill: 4.0 lbs.
Blocking CFFA-4 1
Cold Crack CFFA-6a -10° F
Flex CFFA-10 25,000 cycles
Flammability**
CAL TB 117-2013 Passes
NFPA 260 Class 1
UFAC Class 1
ASTM E-84 Class 1
Boston Fire Code Passes
Federal Aviation Specification Passes
IMO 2010 FTP Part 8, 3.1 Passes
IMO 2010 FTP Part 8, 3.1 & 3.2 Passes
Port Authority of NY/NJ Passes
Recommended Cleaning
Please refer to Detailed Cleaning Instructions.
Although we try hard to make sure colors on our site are accurate, actual colors may vary. Please order samples prior to making a purchase.
Final determination of the suitability of this product for an application rests with the user.
Proposition 65 Warning: Yes
* Abrasion test results exceeding ACT Performance Guidelines are not an indicator of product lifespan. Multiple factors affect fabric durability and appearance retention.
** This term and any corresponding data refer to the typical performance in the specific tests indicated and should not be construed to imply the behavior of this or any other material under actual fire conditions.